NiCoMnAl メタ磁性形状記憶合金の磁場中その場観察

These video files are the supplementary files of "Optical microscopic study on NiCoMnAl metamagnetic shape memory alloy by in situ observation under a pulsed high magnetic field", published in

Co5Al19-thermalCycle.mov
In situ observation of microstructure change under thermal cycle for Ni44.3 Co5.1 Mn31.4 Al19.2.

Co5Al19-9K.mov
In situ observation of microstructure change during the application of magnetic field at 9 K for Ni44.3Co5.1Mn31.4Al19.2.

Co5Al19-25K.mov
In situ observation of microstructure change during the application of magnetic field at 25 K for Ni44.3Co5.1Mn31.4Al19.2.

Co5Al19-50K.mov
In situ observation of microstructure change during the application of magnetic field at 50 K for Ni44.3Co5.1Mn31.4Al19.2.

Co5Al19-75K.mov
In situ observation of microstructure change during the application of magnetic field at 75 K for Ni44.3Co5.1Mn31.4Al19.2.

Co5Al19-100K.mov
In situ observation of microstructure change during the application of magnetic field at 100 K for Ni44.3Co5.1Mn31.4Al19.2.

Co5Al19-125K.mov
In situ observation of microstructure change during the application of magnetic field at 125 K for Ni44.3Co5.1Mn31.4Al19.2.

Co5Al19-150K.mov
In situ observation of microstructure change during the application of magnetic field at 150 K for Ni44.3Co5.1Mn31.4Al19.2.